PLA Glitter is a highly aesthetical PLA based filament with sparkling flakes inside. Slightly modified, the filament retains the typical features of PLA, but is tougher and less brittle. Polylactic acid is one of the most popular materials for 3D printing. Because of the translucency of PLA combined with the flakes, the color saturation can be increased by increasing wall thickness.
PLA Glitter features:
- Beautiful sparkling effect
- Layers are not visible
- Tougher and less brittle compared to regular PLA
- Easy to print
- Low warping
- Limited smell
- Not abrasive
| Size | ø tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
| Description | Testmethod | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,24 g/cc |
| MFR 210°C/2,16 kg | ISO 1133 | 9,56 gr/10 min |
| Tensile strength at yield | ISO 527 | 70 MPa |
| Strain at yield | ISO 527 | 5% |
| Strain at break | ISO 527 | 20% |
| Tensile modulus | ISO 527 | 3120 MPa |
| Impact strength - Charpy method 23˚C | ISO 179 | 3,4 kJ/m² |
| Moisture absorption | ISO 62 | 1968 ppm |
| Vicat softening temp. | ISO 306 | 60°C |
| Glass transition temp. | ISO 11357 | 57°C |
| Description | Testmethod | Typical value |
|---|---|---|
| printing temp. | Internal method | 205±10˚C |
| melting temp. | ISO 11357 | 115±35°C |
Colors:
PLA Glitter is available from stock in the following colors.
For non-stock colors please contact us at info-3dp-mcppnl@mcgc.com.
Packaging:
PLA Glitter is available in nearly any type of packaging and labelling. Ask our team to help you customizing your product.
Additional info:
Due to its low tendency to warp PLA Glitter can also be printed without a heated bed. If you have a heated bed the recommended temperature is ≤60°C.
PLA Glitter can be used on all common desktop FDM or FFF technology 3D printers. It is recommended to purge the nozzle after printing, to prevent build up of flakes for the next print.
Storage:
Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.