3DIAKON™ PMMA or Poly(methyl methacrylate) is a transparent thermoplastic. It is known as having excellent weathering and UV stability combined with excellent impact performance and stiffness. PMMA is characterized as a transparent material (more transparent after post processing) and it is reasonable easy to print.
3DIAKON™
3DIAKON™ features:
• Strong, lightweight and rigid material
• High impact resistant
• Good abrasion resistance
• Transparent and glossy after post processing (sanding)
• UV resistance
• BPA free
| Size | ø tolerance | Roundness |
|---|---|---|
| 1,75mm | ø 0,05mm | 95% |
| 2,85mm | ø 0,10mm | 95% |
| Description | Testmethod | Typical value |
|---|---|---|
| Specific gravity | ISO 1183 | 1,14 g/cm³ |
| MFI 230°C/3,8 kg | ISO 1133 | 1,7 g/10 min |
| Tensile strength at yield | ISO 527 | 43 MPa |
| Impact Strength Charpy method 23°C (notched) | ISO 179 | 6,2 kJ/m² |
| Flexural Modulus | ISO 178 | 1900 MPa |
| Flexural Strength | ISO 178 | 62 MPa |
| Vicat softening temperature | ISO 306B | 91°C |
| Heat deflection temperature HDT B | ISO 75A | 93°C |
| Transmittance | ASTM D1003 | 91.5% |
| Description | Testmethod | Typical value |
|---|---|---|
| Printing temp. | Internal method | 255±10°C |
Colours:
3Diakon™ is available from stock in:
cl1
Packaging:
3Diakon™ is available in the original packaging of Mitsubishi Chemical.
Additional info:
We recommend to print large objects of 3Diakon™ in heated chambers to create a nice and smooth printed object. Storage: Cool and dry (15-25°C), this enhances the shelf life signifi cantly.
Storage:
In order to prevent moisture pick up and contamination, supplied packaging should be kept closed and undamaged. For the same reason, partially used bags should be sealed before re-storage. Allow the material that has been stored elsewhere to adapt to the temperature in the processing room while keeping the bag closed.